Soft phonons and structural phase transitions in La$_{1.875}$Ba$_{0.125}$CuO$_{4}$
Extracted source text ยท arXiv cond-mat/0409775
%% ****** Start of file template.aps ****** %
%%
%%
%% This file is part of the APS files in the REVTeX 4 distribution.
%% Version 4.0 of REVTeX, August 2001
%%
%%
%% Copyright (c) 2001 The American Physical Society.
%%
%% See the REVTeX 4 README file for restrictions and more information.
%%
%
% This is a template for producing manuscripts for use with REVTEX 4.0
% Copy this file to another name and then work on that file.
% That way, you always have this original template file to use.
%
% Group addresses by affiliation; use superscriptaddress for long
% author lists, or if there are many overlapping affiliations.
% For Phys. Rev. appearance, change preprint to twocolumn.
% Choose pra, prb, prc, prd, pre, prl, prstab, or rmp for journal
% Add 'draft' option to mark overfull boxes with black boxes
% Add 'showpacs' option to make PACS codes appear
% Add 'showkeys' option to make keywords appear
%\documentclass[aps,prb,preprint,groupedaddress,showpacs]{revtex4}
%\documentclass[aps,prb,preprint,superscriptaddress,showpacs]{revtex4}
%\documentclass[aps,prb,twocolumn,groupedaddress,showpacs]{revtex4}
%\documentclass[aps,prl,twocolumn,superscriptaddress,showpacs]{revtex4}
\documentclass[aps,prb,twocolumn,superscriptaddress,showpacs]{revtex4}
% You should use BibTeX and apsrev.bst for references
% Choosing a journal automatically selects the correct APS
% BibTeX style file (bst file), so only uncomment the line
% below if necessary.
%\bibliographystyle{apsrev}
\usepackage{color}
\usepackage{graphicx}
\begin{document}
% Use the \preprint command to place your local institutional report
% number in the upper righthand corner of the title page in preprint mode.
% Multiple \preprint commands are allowed.
% Use the 'preprintnumbers' class option to override journal defaults
% to display numbers if necessary
%\preprint{}
\input epsf.sty
%Title of paper
\title{Soft phonons and structural phase transitions in
La$_{1.875}$Ba$_{0.125}$CuO$_{4}$}
% repeat the \author .. \affiliation etc. as needed
% \email, \thanks, \homepage, \altaffiliation all apply to the current
% author. Explanatory text should go in the []'s, actual e-mail
% address or url should go in the {}'s for \email and \homepage.
% Please use the appropriate macro foreach each type of information
% \affiliation command applies to all authors since the last
% \affiliation command. The \affiliation command should follow the
% other information
% \affiliation can be followed by \email, \homepage, \thanks as well.
\author{H.~Kimura}
\email[]{kimura@tagen.tohoku.ac.jp}
%\homepage[]{Your web page}
%\thanks{}
%\altaffiliation{}
\affiliation{Institute of Multidisciplinary Research for Advanced Materials,
Tohoku University, Sendai 980-8577, Japan}
%\author{E. Shiratori}
%\affiliation{Institute of Multidisciplinary Research for Advanced Materials,
%Tohoku University, Sendai 980-8577, Japan}
\author{Y.~Noda}
\affiliation{Institute of Multidisciplinary Research for Advanced Materials,
Tohoku University, Sendai 980-8577, Japan}
\author{H.~Goka}
\affiliation{Institute for Chemical Research, Kyoto University, Gokasho, Uji 610-0011, Japan}
\author{M.~Fujita}
\affiliation{Institute for Material Research, Tohoku University, Sendai 980-8577, Japan}
\author{K.~Yamada}
\affiliation{Institute for Material Research, Tohoku University, Sendai 980-8577, Japan}
\author{G.~Shirane}
\affiliation{Department of physics, Brookhaven National Laboratory, Upton,
New York 11973-5000, U. S. A.}
%Collaboration name if desired (requires use of superscriptaddress
%option in \documentclass). \noaffiliation is required (may also be
%used with the \author command).
%\collaboration can be followed by \email, \homepage, \thanks as well.
%\collaboration{}
%\noaffiliation
\date{\today}
\begin{abstract}
Soft phonon behavior associated with a structural phase transition from
the low-temperature-orthorhombic (LTO) phase ($Bmab$ symmetry) to
the low-temperature-tetragonal (LTT) phase ($P4_{2}/ncm$ symmetry) was investigated
in La$_{1.875}$Ba$_{0.125}$CuO$_{4}$ using neutron scattering. As temperature decreases,
the TO-mode at $Z$-point softens and approaches to zero energy around $T_{\rm d2}=62$~K,
where the LTO -- LTT transition occurs. Below $T_{\rm d2}$, the phonon hardens quite rapidly
and it's energy almost saturates below 50~K. At $T_{\rm d2}$,
the energy dispersion of the soft phonon along in-plane direction significantly changes
while the dispersion along out-of-plane direction is
almost temperature independent.
Coexistence between the LTO phase and the LTT phase,
seen in both the soft phonon spectra and the peak profiles of Bragg reflection, is discussed
in context of the order of structural phase transitions.
\end{abstract}
% insert suggested PACS numbers in braces on next line
\pacs{74.72.Dn, 71.45.Lr, 61.10.-i}
% insert suggested keywords - APS authors don't need to do this
%\keywords{}
%\maketitle must follow title, authors, abstract, \pacs, and \keywords
\maketitle
% body of paper here - Use proper section commands
% References should be done using the \cite, \ref, and \label commands
\section{Introduction}\label{intro}
% Put \label in argument of \section for cross-referencing
%\section{\label{}}
It is well known that La-214 based high-$T_{\rm c}$ cuprates
undergo successive structural phase transitions. On cooling temperature,
the second-order phase transition from the high-temperature tetragonal
(HTT; $I4/mmm$) to the low-temperature orthorhombic (LTO; $Bmab$) occurs.
In some cases, as seen in the
La$_{2-x}$Ba$_{x}$CuO$_{4}$ (LBCO)\cite{Moodenbaugh1988,Axe1989} or the
La$_{2-x-y}$Nd$_{y}$Sr$_{x}$CuO$_{4}$ (LNSCO)\cite{Crawford1991}
systems, further structural phase transitions
from the LTO phase to the low-temperature-less orthorhombic (LTLO; $Pccn$) or to the
low-temperature tetragonal (LTT; $P4_{2}/ncm$) follow the HTT-LTO transition
with decreasing temperature.
These structural phases can be categorized by the pattern of coherent tilting for
CuO$_{6}$ octahedra.
Extensive neutron scattering studies on La$_{2-x}$Sr$_{x}$CuO$_{4}$ (LSCO)
have revealed that a condensation of zone-boundary soft phonons causes
the HTT-LTO structural phase transition, resulting in
a staggered tilting of CuO$_{6}$ octahedra\cite{Birgeneau1987,Boni1988,Thurston1989}.
At the HTT-LTO transition, a degenerate pair of
TO-phonon at $X$-point wave vectors ${\bf q}=(1/2\ \pm1/2\ 0)_{\rm HTT}$,
associated with the tilting motion of CuO$_{6}$ octahedra,
goes soft and split into two modes at ${\it \Gamma}$- and $Z$-points in
the LTO phase. In LSCO system, $Z$-point phonon once hardens just below the transition
temperature but softens again with decreasing
temperature, indicating the structural instability
toward the LTO-LTLO or LTO-LTT transition\cite{Thurston1989}.
Keimer {\it et al}. have experimentally shown in La$_{1.65}$Nd$_{0.35}$CuO$_{4}$ that
the LTO-LTLO transition is also understood as
the ordinary displacive phase transition with the softening of
$Z$-point phonons, which turns into zone-center phonon in the LTLO phase\cite{Keimer1993}
(We call this phonon as ${\it \Gamma}^{\prime}$-point for the sake of convenience).
The summary of the soft phonon behaviors
at several structural phases and definitions of order parameter involving
\{$Q_{1}, Q_{2}$\} or \{$Q, \theta$\} for the tilting of CuO$_{6}$
octahedra\cite{Kimura2004} are schematically shown in Fig.~\ref{fig1}.
The relevance between the structural instability and
the high-$T_{\rm c}$ superconductivity has been also studied intensively in these systems.
It has been reported\cite{Braden1993} that the evolution of
the order parameter of the LTO phase
suppressed below $T_{\rm c}$ in the LSCO of $x=0.13$.
After that it has been discovered\cite{Lee1996,Kimura2000} that
the softening of $Z$-point phonons {\em breaks} at $T_{\rm c}$ in
the LSCO of $x=0.15$ and 0.18.
There facts indicate a competition between the LTO-LTLO (or LTO-LTT)
structural instability and the high-$T_{\rm c}$ superconductivity.
This competitive relation becomes
more apparent in the LBCO and LNSCO systems around 1/8-doping, where the charge stripe
%=========================================================
\begin{figure}[bp]
\centerline{\epsfxsize=3in\epsfbox{fig1.eps}}
\caption{Schematic diagram for the energy of soft phonons as a function of temperature.
Inset depicts the definitions for the tilting of CuO$_{6}$ octahedra.}
\label{fig1}
\end{figure}
%=========================================================
order follows on the LTO-LTT phase transition,
resulting in the suppression of superconductivity\cite{Tranquada1995,Tranquada1996}.
The motivation of the phonon studies in LBCO system is to clarify
the relevance among the low-energy lattice dynamics in the LTT phase,
the high-$T_{\rm c}$ superconductivity, and the charge stripe order.
In the present study, we examined the soft phonon behavior in 1/8-hole doped LBCO
for a wide temperature range including the HTT-LTO and the LTO-LTT structural
phase transition. Our measurement is a first case which observes
the soft phonons associated with the first-order LTO-LTT transition in La-214 system.
%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%
\section{Experimental details}\label{exp}
The single crystal of La$_{1.875}$Ba$_{0.125}$CuO$_{4}$ was grown by
traveling-solvent floating-zone method. Details in growing the single crystal
are described elsewhere\cite{Fujita2004}.
The crystal has a cylindrical shape of which dimension is $\sim8$~mm in diameter with
20~mm height. Note that the crystal in the present study is the very same as
used in the measurements of spin dynamics related with the charge stripe order\cite{Fujita2004}.
Diamagnetic susceptibility was measured with SQUID magnetometer, showing no
bulk superconductivity down to $T=2$~K. We determined the structural phase transition
temperatures for the HTT-LTO (defined as $T_{\rm d1}$) and for
the LTO-LTT (defined as $T_{\rm d2}$) transitions, which is quite
sensitive to the Ba concentration in the crystal.
Figures~\ref{fig2}(a) and (b) are the temperature variations
of peak intensities for $(0\ 1\ 4)$ and $(1\ 1\ 0)$ Bragg reflections
measured with neutron diffraction, which
%=========================================================
\begin{figure}[bp]
\centerline{\epsfxsize=3in\epsfbox{fig2.eps}}
\caption{Temperature dependence of (a); $(0\ 1\ 4)$- and (b);
$(1\ 1\ 0)$-superlattice intensities, which corresponds to the order parameter
for the LTO and the LTT phase, respectively.}
\label{fig2}
\end{figure}
%=========================================================
corresponds to the order parameters for the LTO and the LTT phase, respectively.
As a result, $T_{\rm d1}$ and $T_{\rm d2}$ were obtained as 250~K and 62~K, respectively,
which is almost consistent with the previous results\cite{Axe1989}.
Note that all the Bragg reflections measured at the lowest temperature ($\sim15$~K)
had well defined single peak profiles, showing that
the crystal structure in the lowest temperature phase is not a orthorhombic but
a tetragonal. The lattice parameters obtained at $T=16$~K are $a=b=5.351$~\AA\
and $c=13.239$~\AA.
Inelastic neutron scattering measurements of soft phonons
were performed at triple-axis spectrometer TOPAN of Tohoku University installed at
JRR-3M reactor in Japan Atomic Energy Research Institute (JAERI).
The final energy of neutrons was fixed at $E_{\rm f}=13.5$~meV using
PG(002) analyzer. The sequences of the horizontal collimations were
40'-30'-30'-60' and 30'-30'-30'-60', which yields the energy resolutions of
0.9~meV and 0.8~meV, respectively. A pyrolytic graphite filter and a sapphire cut-off filter
were inserted for scattered and incident beam to reduce the higher-order contamination
of neutrons. The sample was mounted in the $(h\ 0\ l)$ zone.
Since the single crystal has twinned domains at the LTO phase,
both the $(h\ 0\ l)$ and $(0\ k\ l)$ zones are superposed. Throughout this paper,
if no specification is given, the reciprocal space is described
by the reciprocal lattice unit in the LTO ($Bmab$) coordination,
of which definitions are consistent with that in the LTT ($P4_{2}/ncm$) one.
Temperature of the sample is controlled between 16~K and 450~K using
$^{4}$He-closed-cycle cryostat with high-power heater.
%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%
\section{Results and Discussion}\label{res}
\subsection{Soft phonon behavior in wide temperature range}\label{res1}
We measured the energy spectra of phonons around $Q=(3\ 0\ 2)$,
which corresponds to TO-mode at $Z$-point in the LTO phase,
as a function of temperature and as a function of $Q$. All the scans were performed
in a constant-$Q$ mode. Since soft phonons become overdamped in
the vicinity of the structural phase transition
temperature, we could not obtain a well-defined phonon spectra just at
$Q=(3\ 0\ 2)$ (=$Z$-point). Therefore we measured
$(3+q\ 0\ 2)$ mode and determined the phonon dispersion as a function of temperature.
Typical energy spectra of the phonons at $Q=(3.075\ 0\ 2)$
are shown in Fig~\ref{fig3}, taken at several temperatures.
%=========================================================
\begin{figure}[tp]
\centerline{\epsfxsize=3in\epsfbox{fig3.eps}}
\caption{Energy spectra of $(3.075\ 0\ 2)$ phonons at several temperatures.}
\label{fig3}
%\end{figure}
\vfill\vspace*{17mm}
%=========================================================
%=========================================================
%\begin{figure}[t]
\centerline{\epsfxsize=2.3in\epsfbox{fig4.eps}}
\caption{Energy of the four phonon modes as a function of temperature. Lines in the figure
are guides to the eye.}
\label{fig4}
\end{figure}
%=========================================================
The phonon energy $\omega_{\rm ph}$ was extracted by fitting the observed spectra
with the functions of a dumped harmonic oscillator form and
a Gaussian central peak, which convolved with the instrumental resolution.
In these fittings, we assumed $\omega_{\rm ph}$ to be constant within
the energy resolution, meaning that the dispersion of phonons was not considered.
The solid lines in Fig~\ref{fig3} are the results of fittings, which well reproduce
the observed spectra. The arrows in the figures point to
the peak positions determined by the fittings.
Above $T_{\rm d1}$ ($=250$~K), a single phonon peak
is clearly seen, which corresponds to the phonon branch from the degenerate
$X$-point in the HTT phase.
$\omega_{\rm ph}$ decreases as temperature decreases, indicates that
the $X$-point phonon goes soft toward the HTT-LTO phase transtion.
Below $T_{\rm d1}$, in the LTO phase, two phonon peaks appear,
showing that the degenerate $X$-point phonon split into
a lower energy phonon at $Z$-point ($=(3\ 0\ 2)$) and a higher one
at ${\it \Gamma}$-point ($=(0\ 3\ 2)$). Note that the two phonons are observable
simultaneously because of the twinning of $(h\ 0\ l)$ and $(0\ k\ l)$ zones
in the LTO phase.
As seen in the figures, $\omega_{\rm ph}$ for $Z$-point at $T=60$~K increases at
$T=16$~K. This indicates that the LTO-LTT structural phase transitions
occurs and the $Z$-point phonons turn into
${\it \Gamma}^{\prime}$-point around $T=60$~K,
which is consistent with the temperature dependence of
$(1\ 1\ 0)$ super lattice shown in Fig.~\ref{fig2} (b).
Figure~\ref{fig4} shows the representative phonon spectra just at $Q=(3\ 0\ 2)$,
taken below $T_{\rm d2}$. At $T=62$~K, we cannot see clear phonon peak because of the
overdamping of phonons in the vicinity of the structural phase transition. However at $T=52$~K,
below $T_{\rm d2}$, the phonon peak becomes well defined around $\sim5$~meV
and its phonon energy is almost temperature independent down to 16~K.
Figure~\ref{fig5} shows the summary of soft phonon behaviors as
a function of temperature. The phonon energy at $q=0$, defined as $\omega_{0}$,
%=========================================================
\begin{figure}[b]
\centerline{\epsfxsize=3in\epsfbox{fig5.eps}}
\caption{Energy of the four phonon modes as a function of temperature. Lines in the figure
are guides to the eye.}
\label{fig5}
\end{figure}
%=========================================================
was extrapolated from the dispersion relations of $(3+q\ 0\ 2)$ phonons.
Note that $\omega_{0}$ for $(3\ 0\ 2)$ ${\it \Gamma}^{\prime}$-point below 60~K
(denoted by filled squares in Fig~\ref{fig4}) was directly derived from the
$(3\ 0\ 2)$ phonon spectra.
The phonon at degenerate $X$-point (open circles) in the HTT phase
goes soft with decreasing temperature and splits into two modes below
$T_{\rm d1}$, which is due to
the reduction of crystal symmetry into orthorhombic with $Bmab$ space group. Thus
these two modes correspond to zone-boundary phonon at $(3\ 0\ 2)$ $Z$-point
and zone-center one at $(0\ 3\ 2)$ ${\it \Gamma}$-point.
On further cooling temperature, the $Z$-point phonon (open squares)
remains soft and start decreases again in energy while
the ${\it \Gamma}$-point phonon (filled triangles) keeps on
hardening with decreasing temperature, indicating that
the LTO phase evolves and the lattice instability toward the further structural phase
transition increases. These behaviors are qualitatively consistent
with that of La$_{2}$CuO$_{4}$\cite{Thurston1989}.
Below $T\sim60$~K, $Z$-point phonon discontinuously hardens
and its energy becomes almost temperature independent (filled squares),
showing that the LTO-LTT phase transition occurs and the LTT phase
becomes robust rapidly. The phonons at $(0\ 3\ 2)$
${\it \Gamma}$-point (denoted by filled triangles)
show small anomaly around the transition temperature $T_{\rm d2}$,
which indicates that the fluctuation for the tilt amplitude of CuO$_{6}$ octahedra
was also affected by the LTO-LTT transition.
Below $T_{\rm d2}$, $Z$-point becomes zone-center ${\it \Gamma}^{\prime}$-point
and Raman active, because the structural transition from $B$-base centered lattice to
primitive lattice occurs. It should be noted that
the overall behaviors of soft phonons in the present LBCO is
qualitatively consistent with the results for La$_{1.65}$Nd$_{0.35}$CuO$_{4}$,
which shows the second order HTT--LTO--LTLO phase transitions\cite{Keimer1993}.
We systematically measured the phonon spectra of $(3+q\ 0\ 2)$ and $(3\ 0\ 2-q)$ modes
as a function of $q$ in whole temperature range below 450~K
to determine the dispersion relation of the soft phonons.
%=========================================================
\begin{figure}[bp]
\centerline{\epsfxsize=2.5in\epsfbox{fig6.eps}}
\caption{(a), (b); $(3+q\ 0\ 2)$- and (c); $(3\ 0\ 2-q)$-dispersion of the
soft phonons at several temperatures. Solid lines are guides to the eye.}
\label{fig6}
\end{figure}
%=========================================================
We show the dispersion relation as $\omega_{\rm ph}^{2}$ versus $q^{2}$ plot
because the soft phonon dispersion near a structural phase transition can be expressed as
\begin{equation}
\omega_{\rm ph}^{2}=A(T-T_{\rm d1(d2)})+b_{1}q_{1}^{2}+b_{2}q_{2}^{2}+b_{3}q_{3}^{2}
\label{eq1}
\end{equation}
where $b_{1}$, $b_{2}$, and $b_{3}$ are coefficients for $a$-, $b$-, and $c$-axis,
respectively\cite{Thurston1989}.
Figures~\ref{fig5}(a) and (b) show the dispersion of $(3+q\ 0\ 2)$ mode and
Fig.\ref{fig5}(c) shows the dispersion of $(3\ 0\ 2-q)$ mode taken at several temperatures.
Above 60~K, the slope of the dispersion along $a$-axis is
almost temperature independent and $b_{1}$ was obtained as 1100 meV$^{2}$\AA$^{2}$,
of which value are roughly consistent with that for
La$_{1.65}$Nd$_{0.35}$CuO$_{4}$\cite{Keimer1993}.
Furthermore, as seen in Figs.\ref{fig5}(b) and (c), the dispersion at $T=60$~K along
$a$-axis is comparable to that along $c$-axis, indicating that the phonons propagate
isotropically. However, at $T=16$~K, the slope of dispersion along
$a$-axis significantly changes in comparison with
that at $T=60$~K, while the the slope of dispersion along $c$-axis almost unchanges
between 16~K and 60~K.
This interesting feature
is characteristic for the LTT structure because the dispersion of the phonon along $a$-axis
is temperature-independent near the LTO-LTLO structural phase
transition\cite{Keimer1993} in La$_{1.65}$Nd$_{0.35}$CuO$_{4}$.
It might be also suggested that the doped carrier makes the phonon velocity
along $a$-axis reduced and
there exists a possible relation between this modification
and the formation of charge stripes in the LBCO system. Further systematic studies
for soft phonons in this system are required to address this speculation.
%=========================================================
\begin{table}[tbp]
\begin{center}
\setlength{\tabcolsep}{5pt}
\begin{tabular*}{2.1in}{ccc}
\hline
$T$ (K)\phantom{0}&$b_{1}\parallel a$ (meV$^{2}$\AA$^{2}$)\phantom{0}&$b_{3}\parallel c$\\ \hline
60&1100&1080\\
16&290&1370\\ \hline
\end{tabular*}
\end{center}
\caption{
The slope of the phonon dispersion parallel to $a$- and $c$-axis at $T=60$~K and 15~K.}
\label{tab1}
\end{table}
%=========================================================
The coefficients of the dispersion slope $b_{1}$ and $b_{3}$
obtained at $T=60$~K and 16~K are listed in
Table~\ref{tab1}.
\subsection{Coexistence between the LTO and the LTT phases}\label{res2}
We focus on the detailed transition scheme from the LTO to the LTT phase.
Figure~\ref{fig6} is an enlarged figure of Fig.~\ref{fig5} to emphasize the phonon behaviors
around $T_{\rm d2}$. It is clearly seen that the phonon at $Z$-point (open squares)
coexists with that at ${\it \Gamma}^{\prime}$-point (filled squares) between 60~K and 50~K,
which is seen in a region with a gray hatching in the figure. The figure also shows that
the ${\it \Gamma}^{\prime}$-point phonon discontinuously appears, and the $\omega_{0}$ of
$Z$-point phonon gets close to zero quite rapidly but remains at finite energy
below $T_{\rm d2}$, indicating the incomplete softening due to a first-order LTO-LTT
transition. Note that
the energy of the ${\it \Gamma}$-point phonon (filled triangle) gradually
decreases with decreasing temperature where the LTO and the LTT phases coexist.
%=========================================================
\begin{figure}[t]
\centerline{\epsfxsize=3in\epsfbox{fig7.eps}}
\caption{Enlarged view of the energy of the phonon modes as a function of temperature.
Coexistence between the $Z$-point phonon and the ${\it \Gamma}^{\prime}$-point one is seen in
the gray hatched region. Several lines are guides to the eye.}
\label{fig7}
\end{figure}
%=========================================================
This coexistence is apparently seen not only in the phonon spectra but also
in the peak profiles of Bragg reflections.
Figure~\ref{fig7} shows $(3.075\ 0\ 2)$ phonon spectra and $h$-scan profiles
of $(1\ 1\ 0)_{\rm HTT}$ Bragg reflection taken at three
different temperatures between
60~K and 50~K. Mirror index of $(1\ 1\ 0)$ for Bragg reflection is coordinated as
used in the HTT phase, which corresponds to $(2\ 0\ 0)$ in the LTO
coordination. Three peaks are seen in the phonon spectra as shown in Figs.~\ref{fig7}(a)-(c).
The peaks located at the lowest, medium, and the highest energy correspond to
$(3\ 0\ 2)$ $Z$-, $(3\ 0\ 2)$ ${\it \Gamma}^{\prime}$-,
and $(0\ 3\ 2)$ ${\it \Gamma}$-points,
respectively. As temperature decreases, the intensity of the phonon for $Z$-point
decreases whereas that for ${\it \Gamma}^{\prime}$-point increases, and the
${\it \Gamma}^{\prime}$-point phonon finally robust at $T=50$~K.
The present crystal has four domain in the LTO phase, resulting in
the peak splitting into four $(1\ 1\ 0)_{\rm HTT}$ Bragg points.
The geometry of the splitting is illustrated in the inset of Fig.~\ref{fig7}(d).
At 60~K, as shown in Fig.~\ref{fig7}(d), the peak profiles has components of
two main peaks from the LTO domains and a minor peak at $(1\ 1\ 0)_{\rm HTT}$
position which comes from the LTT structure. With decreasing temperature,
the central peak increases but two sideward peaks decreases, and finally, the peak at
$(1\ 1\ 0)_{\rm HTT}$ becomes almost dominant at $T=50$~K, of which behaviors has been
also reported previously\cite{Billinge1993} and
consistent with the present results for soft phonons. Therefore, we conclude that
the LTO phase and the LTT phase competitively coexist and
the volume fraction of each phase changes with decreasing temperature.
We finally introduce a simple discussion by the framework of
Landau phenomenological theory\cite{Axe1989,Ting1990}
%=========================================================
\begin{figure}[t]
\centerline{\epsfxsize=2.8in\epsfbox{fig8.eps}}
\caption{(a)-(c); Energy spectra of $(3.075\ 0\ 2)$ phonons and $h$-scan profiles
of $(1\ 1\ 0)_{\rm HTT}$ Bragg peak taken at three different temperatures
between 60~K and 50~K.}
\label{fig8}
\end{figure}
%=========================================================
to understand the nature of the LTO-LTT transition in this system.
Axe {\it et al}.\cite{Axe1989} proposed a free energy near the structural phase transition
from the LTO to the LTT (LTLO) phase with the expression of
\begin{equation}
F(Q,\theta)=f(Q)+\alpha\cos4\theta+\beta[\cos8\theta-4\cos4\theta]
\label{eq2}
\end{equation}
where $\alpha\sim T_{\rm d2}-T$ near $T_{\rm d2}$.
$Q$ and $\theta$ represent the amplitude of displacement and the rotation angle from
$a$-axis for CuO$_{6}$ octahedra, which is defined
in the inset of Fig.~\ref{fig1}. In this model, $\theta=0^{\circ}$ and $45^{\circ}$
correspond to the LTO and the LTT phase, respectively, and, in the case of
$0^{\circ}<\theta<45^{\circ}$, the LTLO phase appears.
Since the order parameter $Q$, which corresponds to
the tilt amplitude of CuO$_{6}$ octahedra, is almost temperature independent in the vicinity
of $T_{\rm d2}$, the free energy $F$ can be regarded as a function of only $\theta$.
When $\beta>0$, Eq.~\ref{eq2} has
one local minimum at $0^{\circ}<\theta<45^{\circ}$ below $T_{\rm d2}$ and
the second-order phase transition from the LTO to LTLO phase occurs. On the other
hand, for $\beta<0$, two local minimums at $\theta=0^{\circ}$ and $45^{\circ}$
appear in Eq.~\ref{eq2} and the first order LTO-LTT transition occurs,
suggesting that the two phases can be coexist near $T_{\rm d2}$.
Our present results and the previous study\cite{Keimer1993} of
La$_{1.65}$Nd$_{0.35}$CuO$_{4}$ show the validity of this simple model.
%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%
\section{Conclusion}\label{con}
The present study has confirmed the soft phonon behavior of
La$_{1.875}$Ba$_{0.125}$CuO$_{4}$ in the wide temperature range
including the HTT--LTO and the LTO--LTT structural phase transitions,
which can be totally understood by soft-mode transitions.
The dispersion relation of phonons along $a$-axis suddenly changes below $T_{\rm d2}$
while that along $c$-axis is independent of temperature,
which might be characteristic in the LTT structure.
The coexistence of the LTO and the LTT phase observed in both the phonon spectra and
the Bragg peak profiles can be understood as the consequence of the first order
structural phase transition in the frame work of Landau theory.
The relevance between the change of the phonon velocity along $a$-axis in the LTT phase
and the formation of charge stripe order should be clarified in the near future.
%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%
%\section{Conclusion}\label{conc}
%\subsubsection{}
% If in two-column mode, this environment will change to single-column
% format so that long equations can be displayed. Use
% sparingly.
%\begin{widetext}
% put long equation here
%\end{widetext}
% figures should be put into the text as floats.
% Use the graphics or graphicx packages (distributed with LaTeX2e)
% and the \includegraphics macro defined in those packages.
% See the LaTeX Graphics Companion by Michel Goosens, Sebastian Rahtz,
% and Frank Mittelbach for instance.
%
% Here is an example of the general form of a figure:
% Fill in the caption in the braces of the \caption{} command. Put the label
% that you will use with \ref{} command in the braces of the \label{} command.
% Use the figure* environment if the figure should span across the
% entire page. There is no need to do explicit centering.
%\begin{figure}
%\includegraphics{}%
%\caption{\label{fig1}}
%\end{figure}
% Surround figure environment with turnpage environment for landscape
% figure
% \begin{turnpage}
% \begin{figure}
% \includegraphics{}%
% \caption{\label{}}
% \end{figure}
% \end{turnpage}
% tables should appear as floats within the text
%
% Here is an example of the general form of a table:
% Fill in the caption in the braces of the \caption{} command. Put the label
% that you will use with \ref{} command in the braces of the \label{} command.
% Insert the column specifiers (l, r, c, d, etc.) in the empty braces of the
% \begin{tabular}{} command.
% The ruledtabular enviroment adds doubled rules to table and sets a
% reasonable default table settings.
% Use the table* environment to get a full-width table in two-column
% Add \usepackage{longtable} and the longtable (or longtable*}
% environment for nicely formatted long tables. Or use the the [H]
% placement option to break a long table (with less control than
% in longtable).
% \begin{table}%[H] add [H] placement to break table across pages
% \caption{\label{}}
% \begin{ruledtabular}
% \begin{tabular}{}
% Lines of table here ending with \\
% \end{tabular}
% \end{ruledtabular}
% \end{table}
% Surround table environment with turnpage environment for landscape
% table
% \begin{turnpage}
% \begin{table}
% \caption{\label{}}
% \begin{ruledtabular}
% \begin{tabular}{}
% \end{tabular}
% \end{ruledtabular}
% \end{table}
% \end{turnpage}
% Specify following sections are appendices. Use \appendix* if there
% only one appendix.
%\appendix
%\section{}
% If you have acknowledgments, this puts in the proper section head.
\begin{acknowledgments}
The authors thank J.~M.~Tranquada, M.~H\"{u}cker and S.~Wakimoto
for invaluable discussions.
The neutron scattering experiments at JAERI was performed under the PACS
No.~4474 and 4501.
This work was supported in part by a Grant-In-Aid for Young
Scientists B (15740194),
Scientific research B (14340105),
Scientific Research on Priority Areas (12046239), and
Creative Scientific Research (13NP0201) from the Japanese Ministry of Education,
Science, Sports and Culture, and by the US-Japan cooperative research program on
Neutron scattering. Work at Brookhaven National Laboratory is supported by Division of
Material Science, U.~S.~Department of Energy.
% put your acknowledgments here.
\end{acknowledgments}
% Create the reference section using BibTeX:
%\bibliography{references}
\begin{references}
\bibitem{Moodenbaugh1988}A.~R.~Moodenbaugh, Youwen~Xu, M.~Suenaga, T.~J.~Follcerts,
and R.~N.~Shelton,
Phys.~Rev.~B {\bf 38}, 4596 (1988).
\bibitem{Axe1989}J.~D.~Axe, A.~H.~Moudden, D.~Hohlwein, D.~E.~Cox, K.~M.~Mohanty,
A.~R.~Moodenbaugh, and Youwen~Xu,
Phys.~Rev.~Lett. {\bf 62}, 2751, (1989).
\bibitem{Crawford1991}M.~K.~Crawford, R.~L.~Harlow, E.~M.~McCarron,
W.~E.~Farneth, J.~D.~Axe, H.~Chou, and Q.~Huang,
Phys.~Rev.~B {\bf 44}, 7749 (1991).
\bibitem{Birgeneau1987}R.~J.~Birgeneau, C.~Y.~Chen, D.~R.~Gabbe, H.~P.~Jenssen,
M.~A.~Kastner, C.~J.~Peters, P.~J.~Picone, Tineke Thio, T.~R.~Thurston,
H.~L.~Tuller, J.~D.~Axe, P.~B\"{o}ni, and G.~Shirane,
Phys.~Rev.~Lett. {\bf 59}, 1329, (1987).
\bibitem{Boni1988}P.~B\"{o}ni, J.~D.~Axe, G.~Shirane, R.~J.~Birgeneau, D.~R.~Gabbe,
H.~P.~Jenssen, M.~A.~Kastner, C.~J.~Peters, P.~J.~Picone, and T.~R.~Thurston,
Phys.~Rev.~B {\bf 38}, 185 (1988).
\bibitem{Thurston1989}T.~R.~Thurston, R.~J.~Birgeneau, D.~R.~Gabbe, H.~P.~Jenssen,
M.~A.~Kastner, P.~J.~Picone, N.~W.~Preyer, J.~D.~Axe, P.~B\"{o}ni, G.~Shirane, M.~Sato,
K.~Fukuda, and S.~Shamoto,
Phys.~Rev.~B {\bf 39}, 4327 (1989).
\bibitem{Keimer1993}B.~Keimer, R.~J.~Birgeneau, A.~Cassanho, Y.~Endoh, M.~Greven,
M.~A.~Kastner, and G.~Shirane,
Z.~Phys.~B {\bf 91}, 373 (1993).
\bibitem{Kimura2004}$Q_{1}$ and $Q_{2}$
corresponds to displacements along $a$- and $b$-axis in the LTO phase,
which arises from the tilting of CuO$_{6}$ octahedra.
$Q$ can be defined as the vectorial sum of
$Q_{1}$ and $Q_{2}$ with phase angle $\theta$. In this definitions,
$\theta$ can be regarded as the angle between $a$-axis of the LTO phase and
the tilt axis of CuO$_{6}$ octahedra, and $Q$ corresponds to the rotation amplitude
around the tilt axis.
\bibitem{Braden1993}M.~Braden, O.~Hoffels, W.~Schnelle, B.~B\"{u}chner,
G.~Heger, B.~Hennion, I.~Tanaka, and H.~Kojima,
Phys.~Rev.~B {\bf 47}, 12288 (1993).
\bibitem{Lee1996}C.~H.~Lee, K.~Yamada, M.~Arai, S.~Wakimoto, S.~Hosoya, and Y.~Endoh,
Physica~C {\bf 257}, 264 (1996).
\bibitem{Kimura2000}H.~Kimura, K.~Hirota, C.~H.~Lee, K.~Yamada, and G.~Shirane,
J.~Phys.~Soc.~Jpn. {\bf 69}, 851 (2000).
\bibitem{Tranquada1995}J.~M.~Tranquada, B.~J.~Sternlieb, J.~D.~Axe, Y.~Nakamura, and S.~Uchida,
Nature {\bf 375}, 561 (1995).
\bibitem{Tranquada1996}J.~M.~Tranquada, J.~D.~Axe, N.~Ichikawa, Y.~Nakamura, S.~Uchida,
and B. Nachumi,
Phys.~Rev.~B {\bf 54}, 7489 (1996).
\bibitem{Fujita2004}M.~Fujita, H.~Goka, K.~Yamada, J.~M.~Tranquada, and L.~P.~Regnault,
Phys.~Rev.~B {\it in press} (cond-mat/0403396).
\bibitem{Billinge1993}S.~J.~L.~Billinge, G.~H.~Kwei, A.~C.~Lawson, and J.~C.~Thompson,
Phys.~Rev.~Lett. {\bf 71}, 1903, (1993).
\bibitem{Ting1990}W.~Ting, K.~Fossheim, and T.~L\ae greid,
Solid~State~Comm., {\bf 75}, 727 (1990).
\end{references}
\end{document}
\bibitem{Kivelson1998}S.~A.~Kivelson, E.~Fradokin, and V.~J.~Emery,
Nature {\bf 393}, 550 (1998).
\bibitem{Tranquada1997}J.~M.~Tranquada, J.~D.~Axe, N.~Ichikawa, A.~R.~Moodenbaugh,
Y. Nakamura, and S. Uchida,
Phys.~Rev.~Lett. {\bf 78}, 338 (1997).
\bibitem{Moodenbaugh1988}A.~R.~Moodenbaugh, Youwen~Xu, M.~Suenaga, T.~J.~Follcerts,
and R.~N.~Shelton,
Phys.~Rev.~B {\bf 38}, 4596 (1988).
\bibitem{Fujita2002}M.~Fujita, H.~Goka, K.~Yamada, and M.~Matsuda,
Phys.~Rev.~Lett. {\bf 88}, 167008, (2002).
\bibitem{Fujita2002-2}M.~Fujita, H.~Goka, K.~Yamada, and M.~Matsuda,
Phys.~Rev.~B {\bf 66}, 184503 (2002).
\bibitem{Kimura2003}H.~Kimura, H.~Goka, M.~Fujita, Y.~Noda, K.~Yamada, and N.~Ikeda,
Phys.~Rev.~B {\bf 67}, 140503 (2003).
\bibitem{Kimura2003-2}H.~Kimura, {\it et al}. Unpublished.
\bibitem{Zimmermann1998}M.~V.~Zimmermann, A.~Vigliante, T.~Niem\"{o}ller, N.~Ichikawa,
T.~Frello, J.~Madsen, P.~Wochner, S.~Uchida, N.~H.~Andersen, J.~M.~Tranquada, D.~Gibbs, and
J.~R.~Schneider,
Europhys.~Lett. {\bf 41}, 629, (1998).
\bibitem{Noda1998}Y. Noda, K. Ohshima, H. Toraya, K. Tanaka, H. Terauchi,
H. Maeta, and H. Konishi,
J. Synchrotron Radiation {\bf 5}, 485 (1998).
\bibitem{Kimura2003-3}The $q_{\rm ch}$ for
$x=0.075$ has been obtained as $(0.24\ -0.007\ 1/2)$ at the
previous experiment\cite{Kimura2003}.
However, the result of the present study
is more reliable because the instrument resolutions and the statistics are much
more improved than those of the previous work.
\bibitem{Lee1999}Y.~S.~Lee, R.~J.~Birgeneau, M.~A.~Kastner, Y.~Endoh, S.~Wakimoto,
K.~Yamada, R.~W.~Erwin, S.~-H.~Lee, and G.~Shirane,
Phys.~Rev.~B {\bf 60}, 3643 (1999).
\bibitem{Yamase2000-1}H.~Yamase and H.~Kohno,
J.~Phys.~Soc.~Jpn. {\bf 69}, 332 (2000).
\bibitem{Billinge1993}S.~J.~L.~Billinge, G.~H.~Kwei, A.~C.~Lawson, and J.~D.~Thompson,
Phys.~Rev.~Lett. {\bf 71}, 1903, (1993).
\bibitem{Tranquada1999}J.~M.~Tranquada, N.~Ichikawa, and S.~Uchida,
Phys. Rev. B {\bf 59}, 14712 (1999).
\bibitem{Lee2001}S.~-H.~Lee, S.~W.~Cheong, K.~Yamada, and C.~F.~Majkrzak,
Phys. Rev. B {\bf 63}, 060405 (2001).
\bibitem{Zachar2000}O.~Zachar,
Phys. Rev. B {\bf 62}, 13836 (2000).
\bibitem{Kajimoto2000}R.~Kajimoto, T.~Takeshita, H.~Yoshizawa, T.~Tanabe, T.~Katsufuji,
and Y.~Tokura,
Phys. Rev. B {\bf 64}, 144432 (2000).
\bibitem{Kimura2004}H.~Kimura, {\it et al}. Unpublished data.
\bibitem{Lee1996}C.~H.~Lee, K.~Yamada, M.~Arai, S.~Wakimoto, S.~Hosoya, and Y.~Endoh,
Physica~C {\bf 257}, 264 (1996).
\bibitem{Kimura2000}H.~Kimura, K.~Hirota, C.~H.~Lee, K.~Yamada, and G.~Shirane,
J.~Phys.~Soc.~Jpn. {\bf 69}, 851 (2000).
\bibitem{Yamase2000-2}H.~Yamase and H.~Kohno,
J.~Phys.~Soc.~Jpn. {\bf 69}, 2151 (2000).
%
% ****** End of file template.aps ******
The results show that the phonon
rapidly hardens in the LTT phase, which was also seen in
the LTO-LTLO transition of La$_{1.65}$Nd$_{0.35}$CuO$_{4}$\cite{Keimer1993}.
The results are almost consistent with the analogous dispersion in
La$_{2}$CuO$_{4}$\cite{Thurston1989}, indicating that these behaviors
is a common feature of the soft phonons in the HTT and the LTO phase.